LSAT (La₀.₂₉₄Sr₀.₇₀₆Al₀.₆₄₇Ta₀.₃₅₃O₃) Single Crystal Substrate
Price range: د.إ224.06 through د.إ1,156.17
LSAT (La₀.₂₉₄Sr₀.₇₀₆Al₀.₆₄₇Ta₀.₃₅₃O₃) Single Crystal Substrate
Product Overview:
LSAT is a perovskite-structure mixed oxide crystal. It typically has a cubic structure and is used as a substrate for the epitaxial growth of high-temperature superconducting (HTS) films (like YBCO) and magnetic oxide films due to its lattice matching.
Physical Properties:
– Crystal Structure: Cubic System
– Lattice Constant: a = 3.868 Angstrom
– Density: 6.74 g/cm³
– Melting Point: 1840 °C
– Mohs Hardness: 6.5
– Color: Colorless or light yellow (depending on annealing conditions, both are normal)
– Growth Method: Czochralski (CZ)
Standard Specifications:
– Orientation Accuracy: miscut < 0.3° (High precision < 0.1° available upon request)
– Surface Roughness: Ra < 0.5 nm
– Edge Orientation: Available upon request
– Surface Polish: Single-Side or Double-Side Polished
| Option 1 | 10 × 10 × 0.1 mm, (100), Single-Side Polished, 10 × 10 × 0.5 mm, (100), Double-Side Polished, 10 × 10 × 0.5 mm, (100), Single-Side Polished, 10 × 10 × 0.5 mm, (110), Double-Side Polished, 10 × 10 × 0.5 mm, (110), Single-Side Polished, 10 × 10 × 0.5 mm, (111), Double-Side Polished, 10 × 10 × 0.5 mm, (111), Single-Side Polished, 10 × 5 × 0.5 mm, (100), Single-Side Polished, 5 × 5 × 0.5 mm, (100), Double-Side Polished, 5 × 5 × 0.5 mm, (100), Single-Side Polished, 5 × 5 × 0.5 mm, (110), Double-Side Polished, 5 × 5 × 0.5 mm, (110), Single-Side Polished, 5 × 5 × 0.5 mm, (111), Single-Side Polished |
|---|